Generic PPE+PS
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vOeR8T_Generic-PPE-PS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPE+PS This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 - 1.11 | g/cm³ | ASTM D792 |
| 23°C | 1.03 - 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 1.3 - 18 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 5.70 - 18.6 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.59 - 0.61 | % | ASTM D955 |
| Transverse flow : 23°C | 0.56 - 0.60 | % | ASTM D955 |
| 23°C | 0.58 - 0.61 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.054 - 0.10 | % | ASTM D570 |
| 23°C, 24 hr | 0.059 - 0.10 | % | ISO 62 |
| Saturated, 23°C | 0.060 - 0.25 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.045 - 0.067 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 113 - 124 | ASTM D785 | |
| Ball Indentation Hardness | 70.0 - 114 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2040 - 2890 | MPa | ASTM D638 |
| 23°C | 2170 - 2700 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 32.7 - 81.7 | MPa | ASTM D638 |
| Yield, 23°C | 35.8 - 76.4 | MPa | ISO 527-2 |
| Fracture, 23°C | 38.5 - 62.4 | MPa | ASTM D638 |
| Fracture, 23°C | 35.0 - 80.9 | MPa | ISO 527-2 |
| 23°C | 39.6 - 70.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.0 - 5.3 | % | ASTM D638 |
| Yield, 23°C | 1.7 - 5.1 | % | ISO 527-2 |
| Fracture, 23°C | 1.7 - 83 | % | ASTM D638 |
| Fracture, 23°C | 3.3 - 31 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 9.0 - 31 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1920 - 2840 | MPa | ASTM D790 |
| 23°C | 1920 - 3050 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 53.1 - 111 | MPa | ASTM D790 |
| 23°C | 57.5 - 113 | MPa | ISO 178 |
| Yield, 23°C | 52.4 - 155 | MPa | ASTM D790 |
| Fracture, 23°C | 47.6 - 136 | MPa | ASTM D790 |
| Coefficient of Friction | 0.19 - 0.28 | ASTM D1894 | |
| Taber Abrasion Resistance (23°C) | 35.0 - 78.9 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.3 - 21 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 17 - 150 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 31 - 380 | J/m | ASTM D256 |
| 23°C | 3.8 - 26 | kJ/m² | ISO 180 |
| Notched Izod Impact (23°C) | 7.00 - 18.0 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact | |||
| 23°C | 160 - 2600 | J/m | ASTM D256 |
| 23°C | 17 - 180 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 9.03 - 54.8 | J | ASTM D3763 |
| Dart Drop Impact (23°C) | 13.6 - 17.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 87.6 - 161 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 95.0 - 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 72.6 - 150 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 70.0 - 148 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 94.4 - 168 | °C | ASTM D1525 |
| -- | 91.0 - 164 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 5.9E-5 - 9.5E-5 | cm/cm/°C | ASTM E831 |
| Flow | 6.6E-5 - 9.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 5.5E-5 - 9.6E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 5.6E-5 - 9.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.18 - 0.27 | W/m/K | ISO 8302 |
| RTI Elec | 50.0 - 112 | °C | UL 746 |
| RTI Imp | 50.0 - 106 | °C | UL 746 |
| RTI | 50.0 - 112 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 5.1E+3 - 3.1E+16 | ohms | ASTM D257 |
| -- | 2.0E+3 - 3.1E+16 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+3 - 3.8E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+15 - 3.9E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 17 - 36 | kV/mm | ASTM D149 |
| 23°C | 15 - 35 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 2.51 - 2.91 | ASTM D150 | |
| 23°C | 2.80 - 2.90 | IEC 60250 | |
| 23°C | 2.70 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 4.0E-4 - 0.067 | ASTM D150 | |
| 23°C | 4.0E-4 - 4.1E-3 | IEC 60250 | |
| Comparative Tracking Index | 211 - 286 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 952 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 697 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | |||
| -- | 22 - 39 | % | ASTM D2863 |
| -- | 20 - 34 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | 66.0 - 100 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 74.4 - 111 | °C | |
| Drying Time | 2.0 - 3.7 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.019 - 0.020 | % | |
| Suggested Shot Size | 50 | % | |
| Hopper Temperature | 70.0 - 90.0 | °C | |
| Rear Temperature | 209 - 292 | °C | |
| Middle Temperature | 248 - 295 | °C | |
| Front Temperature | 257 - 300 | °C | |
| Nozzle Temperature | 248 - 313 | °C | |
| Processing (Melt) Temp | 263 - 315 | °C | |
| Mold Temperature | 54.7 - 101 | °C | |
| Injection Pressure | 55.0 - 85.8 | MPa | |
| Back Pressure | 0.511 - 0.517 | MPa | |
| Screw Speed | 58 - 60 | rpm | |
| Vent Depth | 0.044 - 0.045 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPE+PSThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 - 110 | °C | |
| Drying Time | 2.0 - 3.5 | hr | |
| Suggested Max Moisture | 2.0E-4 - 0.050 | % | |
| Cylinder Zone 1 Temp. | 202 - 260 | °C | |
| Cylinder Zone 2 Temp. | 226 - 260 | °C | |
| Cylinder Zone 3 Temp. | 188 - 280 | °C | |
| Cylinder Zone 4 Temp. | 225 - 280 | °C | |
| Cylinder Zone 5 Temp. | 254 - 260 | °C | |
| Adapter Temperature | 248 - 280 | °C | |
| Melt Temperature | 207 - 281 | °C | |
| Die Temperature | 204 - 280 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPE+PSThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Impact 825E | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Nycal鈩?1820RMC40 Bk-1 | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| ANYPOL CL-200LL | SH Energy & Chemical | PS (EPS) | ANYPOL |
| Eco Cool Plus SCMP 89 | EcolBiotech Co., Ltd | PBT | Eco Cool Plus |
| DOWLEX™ GM 8071G | The Dow Chemical Company | LLDPE | DOWLEX™ |