Glass-fiber reinforced polyphthalamide compound especially suitable for plastic and rubber composites VESTAMID HTplus R1033 is a glass-fiber reinforced (30%), heat-stabilized polyphthalamide compound (PPA) especially suitable for the production of rubber and plastic composites. This process is patented by Evonik Degussa GmbH. Parts of VESTAMID HTplus R1033 can be directly bonded to rubber, e. g., HNBR or FPM, without using any adhesives or adhesion promotors. This compound is especially for manufacturing parts subjected to high temperature. VESTAMID HTplus R1033 is supplied as cylindrical pellets in polyethylene packaging. Drying at 120°C for at least 4 hours before processing is recommended. For information about processing of VESTAMID HTplus R1033, please contact our experts in the department Applications Technology of the High Performance Polymers Business Line.

Message

Glass-fiber reinforced polyphthalamide compound especially suitable for plastic and rubber composites

VESTAMID HTplus R1033 is a glass-fiber reinforced (30%), heat-stabilized polyphthalamide compound (PPA) especially suitable for the production of rubber and plastic composites. This process is patented by Evonik Degussa GmbH.

Parts of VESTAMID HTplus R1033 can be directly bonded to rubber, e. g., HNBR or FPM, without using any adhesives or adhesion promotors.

This compound is especially for manufacturing parts subjected to high temperature.

VESTAMID HTplus R1033 is supplied as cylindrical pellets in polyethylene packaging.

Drying at 120°C for at least 4 hours before processing is recommended.

For information about processing of VESTAMID HTplus R1033, please contact our experts in the department Applications Technology of the High Performance Polymers Business Line.

General Information
Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Additive	Heat Stabilizer
Features	Bondability Heat Stabilized High Heat Resistance
Uses	Compounding
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Density	1.44	g/cm³	ISO 1183

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	11000	MPa	ISO 527-2
Tensile Stress (Break)	170	MPa	ISO 527-2
Tensile Strain (Break)	2.0	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-40°C, Complete Break	6.0	kJ/m²
23°C, Complete Break	7.0	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
-40°C, Complete Break	34	kJ/m²
23°C, Complete Break	38	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature
--	305	°C	ISO 306/A
--	275	°C	ISO 306/B
Melting Temperature	300 to 315	°C	ISO 11357-3

Resin Grade	Manufacturer	Category	Trademark
AIE PBT 30G3	Asia International Enterprise (Hong Kong) Limited	PBT	AIE PBT
CEPLA CW-462E	CEPLA Co., LTD	PP, Unspecified	CEPLA
CYCOLAC™ DL100 resin	SABIC Innovative Plastics Europe	ABS	CYCOLAC™
Polimid A SG Y	Poliblend S.p.a.	Nylon 66	Polimid A
Hifax CA 1210 G 1740	LyondellBasell Industries	PP Copolymer	Hifax