Iupital® A25-03
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vKp8Zs_Iupital-A25-03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupital®A25-03 is a polyoxymethylene (POM) copolymer material,. This product is available in North America, Europe or Asia Pacific region. The processing method is injection molding. Iupital®The main features of the A25-03 are:
Iupital®The typical application fields of A25-03 are: automobile industry |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.00 mm) | 2.1 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.22 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3050 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 69.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 11 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 35 | % | ISO 527-2 |
| Flexural Modulus | 2950 | MPa | ISO 178 |
| Flexural Stress | 98.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 250 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 105 | °C | ISO 75-2/A |
| Melting Temperature | 170 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 175 | °C | |
| Middle Temperature | 185 | °C | |
| Front Temperature | 195 | °C | |
| Nozzle Temperature | 180 - 210 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 80 - 120 | rpm |
| Note Message | |
|---|---|
| 1 . | 60% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4596 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TECHLEN M1250 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| Colorite 12 Series 9512 | Colorite Polymers | PVC, Unspecified | Colorite 12 Series |
| Hanwha Total PP FH51 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Karina COMP. PVC CRYSTAL - E 90/212-DA-IS-SI-AT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |