NEALID XG400
| Category: | Nylon+Olefin , Polyamide + Polyolefin |
| Manufacturer: | AD majoris |
| Trademark: | NEALID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vHp6LB_NEALID-XG400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NEALID XG400 is a 40 % glass fibre reinforced polyamide alloy intended for Injection moulding. APPLICATIONS NEALID XG400 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. NEALID XG400 is available in both natural (NEALID XG400) and black (NEALID XG400-8229) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 to 0.60 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.90 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11000 | 10000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 125 | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 9550 | 8600 | MPa | ISO 178 |
| Flexural Stress | 200 | 180 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 12 | 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 36 | 38 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 246 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 230 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+15 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+15 | 1.0E+15 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 285 to 300 | °C | |
| Middle Temperature | 280 to 295 | °C | |
| Front Temperature | 275 to 290 | °C | |
| Nozzle Temperature | 265 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PP PRM4201 | Shandong Dongchen Engineering Plastics Co., Ltd. | PP, Unspecified | Shandong PP |
| Sumikon® EME-6310HX | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| Kotex KG-20F10 | Kotec Corporation | PC | Kotex |
| Sylvin 9777-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LG ABS SG175H | LG Chem Ltd. | ABS | LG ABS |