Tenac™-C CF452
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™-C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vHltsF_Tenac--C-CF452.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™-C CF452 is an Acetal (POM) Copolymer product filled with carbon fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™-C CF452 include engineering/industrial parts and housings. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.30 to 0.60 | % | |
| Across Flow | 0.80 to 1.2 | % | |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7500 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Break | 110 | MPa | ISO 527-2 |
| -- | 101 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break | 5.0 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 7000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 155 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 33 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 162 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 165 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 161 | °C | ISO 75-2/A |
| CLTE | |||
| Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Flow | 6.0E-5 to 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS 3302 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| TPSiV™ 4100-70A | Multibase, A Dow Corning Company | TPSiV | TPSiV™ |
| Fixmaster Roof and Gutter Sealant | Loctite® | PUR, Unspecified | Fixmaster |
| Karina WHITE PVC COMPOUND 833D10/184-AY-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYCOMPO PE 7000F | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |