Skyrol® SL10S
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | SKC Inc. |
| Trademark: | Skyrol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vHPcAM_Skyrol-SL10S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Skyrol® SL10S is a coextruded polyester film with heat sealable layer on one side, and slip treated on the other side for handling purposes . It is specially developed for use in various packaging applications. SL10S has a wide range of heat sealing temperature and a good adhesion to steel lamination. SL10S complies with FDA regulation FDA 21 CFR 117.1630. It is available in the thickness ranging from 48 to 142 gauge. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.40 | g/cm³ | ASTM D1505 |
| Molding Shrinkage | Internal Method | ||
| Flow : 150°C, 30 min, 0.0150 mm | 1.8 | % | |
| Flow : 150°C, 30 min, 0.0300 mm | 1.9 | % | |
| Across Flow : 150°C, 30 min, 0.0150 mm | 0.50 | % | |
| Across Flow : 150°C, 30 min, 0.0300 mm | 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 2 | 0.30 | ||
| vs. Itself - Dynamic 3 | 0.40 | ||
| vs. Itself - Static 4 | 0.50 | ||
| vs. Itself - Static 5 | 0.40 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 15 µm | 214 | MPa | |
| MD : Yield, 30 µm | 248 | MPa | |
| TD : Yield, 15 µm | 200 | MPa | |
| TD : Yield, 30 µm | 221 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 15 µm | 130 | % | |
| MD : Break, 30 µm | 120 | % | |
| TD : Break, 15 µm | 130 | % | |
| TD : Break, 30 µm | 140 | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | ASTM D1003 | ||
| 15.0 µm | 3.5 | % | |
| 30.0 µm | 3.8 | % |
| Note Message | |
|---|---|
| 1 . | 30 µm |
| 2 . | 30 µm |
| 3 . | 15 µm |
| 4 . | 15 µm |
| 5 . | 30 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PA6 L BLK | RTP Company | Nylon 6 | RTP |
| Quantum Composites QC-2430 | Quantum Composites Inc. | Phenolic | Quantum Composites |
| Sylvin 9441-50 Natural | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| Moplen S33LS | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| LUVOCOM® 1/GF/40/TF/13 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |