SABIC® LLDPE 318BE
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vH8tOq_SABIC-LLDPE-318BE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LLDPE 318BE is a butene linear low density polyethylene resin typically designed for easy processing and specially formulated for optimum thermal stability at high temperatures used in cast film extrusion. Cast film produced from SABIC® LLDPE 318BE exhibit very good optical properties, puncture resistance and tear strength. The suffix E denotes European origin. Application SABIC® LLDPE 318BE resin is typically used for hand and pallet stretch wrap. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.8 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Elastic Recovery - Cast Film (20.0 µm) | 52 | % | ASTM D5459 |
| Protrusion Puncture Resistance - Cast Film (20.0 µm) | 2.00 | J | ASTM D5748 |
| Retention Force - 60 sec (20.0 µm) 1 | 890 | g | |
| Stress Retention - Cast Film (20.0 µm) | 78 | % | ASTM D5459 |
| Ultimate Pre-stretch Level - Cast Film (20.0 µm) | 310 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dart Impact - Cast Film (20.0 µm) | 26.0 | J/cm | ISO 7765-2 |
| Peel Cling 2 | ASTM D5458 | ||
| 0% pre-stretch : 20.0 µm | 127.5 | g/2.5 cm | ASTM D5458 |
| 200% pre-stretch : 20.0 µm | 76.5 | g/2.5 cm | ASTM D5458 |
| Tear Strength - TD (20.0 µm) 3 | 140.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 102 | °C | ISO 306/A |
| Melting Temperature (DSC) | 121 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm, Cast Film) | 91 | ASTM D2457 | |
| Haze (20.0 µm, Cast Film) | 2.1 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Properties are determined on 20 µm cast stretch film produced on a 2 m commercial cast stretch line: melt temperature 270°C, chill roll temperature 20°C and line speed of 450 m/min. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 250 - 300 | °C |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| 2 . | Cast Film |
| 3 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 9180 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Ebalta Xiameter RTV 4234-T4 | Ebalta Kunststoff GmbH | Silicone Rubber, RTV-1 | Ebalta |
| PALPROP® R C 25 | pal plast GmbH | PP Impact Copolymer | PALPROP® |
| Hostacom T 30 T2 NERO | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Sylvin 5153-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |