Ketron® PEEK CM CA30
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Ketron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vGNbkD_Ketron-PEEK-CM-CA30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ketron® PEEK CM CA30 is a Polyetheretherketone (PEEK) product filled with 30% carbon fiber. It can be processed by compression molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.15 | % | |
| Saturation | 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 108 | ||
| R-Scale | 125 | ||
| Durometer Hardness (Shore D) | 91 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9650 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 159 | MPa | ASTM D790 |
| Compressive Modulus | 4000 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 193 | MPa | ASTM D695 |
| Shear Strength | 75.8 | MPa | ASTM D732 |
| Coefficient of Friction (vs. Steel - Static) | 0.24 | Internal Method | |
| Wear Factor | 210 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 75 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 232 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 249 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.596 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 340 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 4.1E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.92 | W/m/K | ASTM F433 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V909 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Silopren® Gel 6209FC | Momentive Performance Materials Inc. | Silicone Gel | Silopren® |
| Comco PA 6 G MOS 2 | Comco-Plastic GmbH | Nylon 6 | Comco |
| EL-Lene™ M3204RU | SCG Chemicals Co., Ltd. | LLDPE | EL-Lene™ |
| Sylvin 9812-95 Red 683 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |