Zytel® 73G15L NC010
| Category: | Nylon 6 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vF4bEO_Zytel-73G15L-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% Glass Reinforced Polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.23 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 7.6 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.5 | -- | % | |
| Viscosity Number | 150 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6000 | 3500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 135 | 72.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | 10 | % | ISO 527-2 |
| Flexural Modulus | 5000 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 6.0 | -- | kJ/m² | |
| -30°C | 6.0 | 14 | kJ/m² | |
| 23°C | 7.0 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 45 | 54 | kJ/m² | |
| 23°C | 50 | 95 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 5.0 | -- | kJ/m² | |
| -30°C | 5.0 | -- | kJ/m² | |
| 23°C | 6.0 | 12 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -40°C | 40 | -- | kJ/m² | |
| 23°C | 45 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | -- | °C | ISO 306/B50 |
| Melting Temperature 1 | 221 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 3.7E-5 | -- | cm/cm/°C | |
| Transverse | 1.1E-4 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | 25 | -- | mm/min | ISO 3795 |
| Flammability Classification (1.50 mm) | HB HB | -- | IEC 60695-11-10, -20 | |
| Oxygen Index | 21 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Density | 1.07 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2470 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.19 | -- | W/m/K |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Emission of Organic Compounds | 8.50 | -- | µgC/g | VDA 277 |
| Odor | 4 | -- | VDA 270 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | DS |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 5376FFR | Colorite Polymers | PVC, Unspecified | Unichem |
| ALCOM® PC 740/4 UV WT1370-07LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| LEXAN™ HF1140R resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LG ABS TR558A | LG Chem Ltd. | ABS | LG ABS |
| Pharmalene® FL 20 PH | Versalis S.p.A. | LDPE | Pharmalene® |