Terralene® PP 2509
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Terralene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vExu3g_TerralenePP2509.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylen copolymer blend with biobased high density polyethylene. The biobased carbon content (BCC) is 33 % (determined according to ASTM D6866). Suitable for injection moulding applications such as bins. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.916 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 42 - 47 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 31.0 - 35.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 910 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 20.5 | MPa | ISO 527-2 |
| Fracture | 9.00 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 140 | % | ISO 527-2 |
| Tensile Strain at Tensile Strength | 15 | % | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(Complete Break) | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 2 | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 117 | °C | ISO 306/A |
| Melting Temperature | 160 - 165 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 | °C | |
| Middle Temperature | 190 | °C | |
| Front Temperature | 200 | °C | |
| Nozzle Temperature | 205 | °C | |
| Mold Temperature | 40 | °C |
| Injection instructions |
|---|
| Holding Pressure: 40 - 70 %Melt cushion (of volume): 3 - 10 %Cooling time: 15 secMax. dwell time: 300 sec. |
| Note Message | |
|---|---|
| 1 . | RT |
| 2 . | RT |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Avalon 22 | Greene, Tweed & Co. | PTFE | Avalon |
| Elastollan® LP 9307 | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| KumhoSunny ABS H2938Z | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Karina IVORY PVC COMPOUND -E 105440-35/ 1-Y-IS-SD-LM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 4299-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |