Stirofor® HI-V0 NATURALE
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Stirofor® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vEncM0_Stirofor-HI-V0-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hi-impact polystyrene, flame retardant grade UL94 V-2/V-0 |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.50 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 30.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 20 | % | ASTM D638 |
| Flexural Modulus | 2300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 77.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 1 |
| Ball Pressure Test (75°C) | Pass | IEC 335 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Needle Flame Test | Pass | IEC 60695-11-5 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 23 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 160 | °C | |
| Middle Temperature | 170 | °C | |
| Front Temperature | 180 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PS 535 | Nizhnekamskneftekhim Inc. | PS (GPPS) | NEFTEKHIM PS |
| Nipol® LX552 | Zeon Corporation | Latex | Nipol® |
| ESTAPROP 0540 GFC V0 | Cossa Polimeri S.r.l. | PP, Unspecified | ESTAPROP |
| INEOS PP R35C-00 | INEOS Olefins & Polymers USA | PP Random Copolymer | INEOS PP |
| LNP™ LUBRICOMP™ PDXF89080 compound | SABIC Innovative Plastics | PE, Unspecified | LNP™ LUBRICOMP™ |