Badalac® ABS 20 GK30
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Bada AG |
| Trademark: | Badalac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v9X08z_Badalac-ABS-20-GK30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Easy flowing, 30% glass beads filled standard injection moulding grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.16 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 12.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.80 | % | |
| Equilibrium, 23°C, 50% RH | 0.18 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 3150 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Yield, 23°C) | 48.0 | MPa | ISO 527-2/50 |
| Tensile Strain 3(Yield, 23°C) | 2.5 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break 4(23°C) | 7.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5(23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 6(23°C) | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed | 106 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 101 | °C | ISO 75-2/A |
| Vicat Softening Temperature 8 | |||
| -- | 108 | °C | ISO 306/A50 |
| -- | 98.0 | °C | ISO 306/B50 |
| Maximum Service Temperature - 20000 hrs | 80 | °C | IEC 216 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 9 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity 10 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength 11 | 37 | kV/mm | IEC 60243-1 |
| Relative Permittivity 12(1 MHz) | 2.80 | IEC 60250 | |
| Dissipation Factor 13(1 MHz) | 7.9E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 14(0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | Test Specimen accordng to ISO 3167, Type A |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 110x10x4 mm |
| 8 . | Compound for moulding |
| 9 . | 80x80x1 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| 14 . | 125x13x0.8 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 884 DEL | RTP Company | Acetal (POM) Homopolymer | RTP |
| Zetpol® 4310EP | Zeon Chemicals L.P. | NBR | Zetpol® |
| HIDEN® U090 L | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE, UHMW | HIDEN® |
| KEBAFORM® C 274 VT | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| KMI PP KM-053JB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |