VICTREX® PEEK 650CA30

Category:	PEEK , Polyetheretherketone
Manufacturer:	Victrex plc
Trademark:	VICTREX® PEEK
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	v99nh2_VICTREX-PEEK-650CA30.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, low flow, FDA food contact compliant, colour black.

Applications for higher strength and stiffness in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.

General Information
Filler / Reinforcement	Carbon fiber reinforced material, 30% filler by weight
Features	Semicrystallization Low friction coefficient Rigidity, high High strength Low liquidity Good chemical resistance Good wear resistance Compliance of Food Exposure
Agency Ratings	FDA Food Exposure, Not Rated
Appearance	Black
Forms	Particles
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Density ¹	1.40	g/cm³	ISO 1183
Spiral Flow ²			Internal method
-- ³	8.00	cm	Internal method
-- ⁴	37.5	cm	Internal method
Molding Shrinkage ⁵			ISO 294-4
Vertical flow direction	0.50	%	ISO 294-4
Flow direction	0.10	%	ISO 294-4
Water Absorption			ISO 62
23°C, 24 hr, 3.20 mm	0.040	%	ISO 62
Equilibrium, 23°C, 50% RH	0.30	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	27000	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Fracture, 23°C	250	MPa	ISO 527-2
Fracture, 125°C	150	MPa	ISO 527-2
Fracture, 175°C	85.0	MPa	ISO 527-2
Fracture, 275°C	50.0	MPa	ISO 527-2
Tensile Strain (Break, 23°C)	2.2	%	ISO 527-2
Flexural Modulus (23°C)	23000	MPa	ISO 178
Flexural Stress			ISO 178
23°C	370	MPa	ISO 178
125°C	250	MPa	ISO 178
175°C	120	MPa	ISO 178
275°C	60.0	MPa	ISO 178
Compressive Stress			ISO 604
23°C	280	MPa	ISO 604
120°C	180	MPa	ISO 604
200°C	60.0	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	11	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	60	kJ/m²	ISO 179/1U
Notched Izod Impact (23°C)	12	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength (23°C)	60	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	333	°C	ISO 75-2/Af
Glass Transition Temperature	143	°C	ISO 11357-2
Melting Temperature	343	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : > 143°C	6.0E-6	cm/cm/°C	ISO 11359-2
Flow : < 143°C	6.0E-6	cm/cm/°C	ISO 11359-2
Lateral : < 143°C	5.0E-5	cm/cm/°C	ISO 11359-2
Lateral : > 143°C	1.4E-4	cm/cm/°C	ISO 11359-2
Specific Heat (23°C)	1800	J/kg/°C	DSC
Thermal Conductivity (23°C)	0.95	W/m/K	ISO 22007-4

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity ⁶(23°C)	1.0E+5	ohms·cm	IEC 60093

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (420°C)	775	Pa·s	ISO 11443

Injection	Nominal Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	3.0 - 5.0	hr
Hopper Temperature	< 100	°C
Rear Temperature	390	°C
Middle Temperature	405	°C
Front Temperature	410	°C
Nozzle Temperature	415	°C
Mold Temperature	180 - 210	°C

Injection instructions
Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness

Note Message
1 .	Crystalline
2 .	Mold temperature: 200°C, melt temperature: 415°C
3 .	1 mm
4 .	3 mm
5 .	415°C nozzle, 200°C tool
6 .	1V

Resin Grade	Manufacturer	Category	Trademark
SLOVALEN® PC 51 T 20	Plastcom	PP, Unspecified	SLOVALEN®
Cevian® K18	PlastxWorld Inc.	Acrylic, Unspecified	Cevian®
KOPA® KN126K	Kolon Plastics, Inc.	Nylon 6	KOPA®
Karina CREPE PVC COMPOUND -E 601D22/ 15	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
RTP 899 X 141392 B NS	RTP Company	Acetal (POM) Copolymer	RTP