TAFMER™ XM-7070

Category:	PAO , Polyalphaolefin
Manufacturer:	Mitsui Chemicals America, Inc.
Trademark:	TAFMER™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	v8QRKF_TAFMER-XM-7070.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
TAFMER™ XM is a superior, low crystalline copolymer of propylene and alpha-olefin which is perfect for biaxially oriented polypropylene (PP) and cast film sealant as well as a resin modifier for polyolefins. TAFMER XM is developed with Metallocene catalyst. The material has excellent low temperature sealability, good sealing performance in a wide temperature range and good anti-blocking properties. As a heat seal layer for OPP film, TAFMER XM is an excellent package sealer for chocolates, cookies and crackers among other items. In addition, the low temperature shrink characteristics of PP can be improved with TAFMER XM.

Message

TAFMER™ XM is a superior, low crystalline copolymer of propylene and alpha-olefin which is perfect for biaxially oriented polypropylene (PP) and cast film sealant as well as a resin modifier for polyolefins. TAFMER XM is developed with Metallocene catalyst. The material has excellent low temperature sealability, good sealing performance in a wide temperature range and good anti-blocking properties. As a heat seal layer for OPP film, TAFMER XM is an excellent package sealer for chocolates, cookies and crackers among other items. In addition, the low temperature shrink characteristics of PP can be improved with TAFMER XM.

General Information
Features	High Clarity High Gloss High Hardness High Heat Resistance High Scratch Resistance Hot Tack Strength Low Temperature Heat Sealability Low to No Odor Low to No Taste
Uses	Film Packaging Sealants Shrink Wrap
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	7.0	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	52		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	290	MPa	ASTM D638
Tensile Strength			ASTM D638
Yield	11.0	MPa
Break	34.0	MPa
Tensile Elongation (Break)	> 600	%	ASTM D638

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	67.0	°C	ASTM D1525
Melting Temperature	75.0	°C	ASTM D2117

Resin Grade	Manufacturer	Category	Trademark
RTP 2100 AR 15 TFE 15	RTP Company	PEI	RTP
Moldex® QS262D/QCM240	Mitsubishi Chemical Corporation	Polyolefin, Unspecified	Moldex®
Gebalon 10-141 HI	geba Kunststoffcompounds GmbH	PC	Gebalon
Moplen HP2619	LyondellBasell Industries	PP Homopolymer	Moplen
XENOY™ 1760 resin	SABIC Innovative Plastics Asia Pacific	PC+PBT	XENOY™