Order Products : sales@su-jiao.com

VICTREX® PEEK 90GL60

Category:	PEEK , Polyetheretherketone
Manufacturer:	Victrex plc
Trademark:	VICTREX® PEEK
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	v7FRFN_VICTREX-PEEK-90GL60.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High performance thermoplastic material, 60% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, standard flow, FDA food contact compliant, colour natural/beige.

Applications where higher strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 60% filler by weight
Features	Semicrystallization High strength Good disinfection Good liquidity Good chemical resistance Compliance of Food Exposure
Agency Ratings	FDA Food Exposure, Not Rated
Appearance	Beige Natural color
Forms	Particles
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density ¹	1.83	g/cm³	ISO 1183
Spiral Flow ²	10.0	cm	Internal method
Molding Shrinkage ³			ISO 294-4
Vertical flow direction : 190°C	0.60	%	ISO 294-4
Flow direction : 190°C, 3.00mm	0.30	%	ISO 294-4
Water Absorption			ISO 62
23°C, 24 hr, 3.20 mm	0.020	%	ISO 62
Balance, 23°C, 3.20mm, 50% RH	0.40	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 23°C)	87		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	25000	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Fracture, 23°C	230	MPa	ISO 527-2
Fracture, 125°C	145	MPa	ISO 527-2
Fracture, 175°C	90.0	MPa	ISO 527-2
Fracture, 225°C	70.0	MPa	ISO 527-2
Fracture, 275°C	50.0	MPa	ISO 527-2
Tensile Strain (Break, 23°C)	1.5	%	ISO 527-2
Flexural Modulus (23°C)	24000	MPa	ISO 178
Flexural Stress (23°C)	350	MPa	ISO 178
Compressive Stress			ISO 604
23°C	230	MPa	ISO 604
120°C	140	MPa	ISO 604
200°C	65.0	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	11	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength (23°C)	45	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	343	°C	ISO 75-2/A
Glass Transition Temperature	143	°C	ISO 11357-2
Melting Temperature	343	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : < 143°C	1.3E-5	cm/cm/°C	ISO 11359-2
Flow : > 143°C	1.5E-5	cm/cm/°C	ISO 11359-2
Lateral : < 143°C	3.0E-5	cm/cm/°C	ISO 11359-2
Lateral : > 143°C	7.0E-5	cm/cm/°C	ISO 11359-2
Specific Heat (23°C)	1700	J/kg/°C	DSC
Thermal Conductivity (23°C)	0.46	W/m/K	ISO 22007-4

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+16	ohms·cm	IEC 60093
Dielectric Strength (2.50 mm)	22	kV/mm	IEC 60243-1
Dielectric Constant (23°C, 1 kHz)	3.80		IEC 60250
Dissipation Factor (23°C, 1 MHz)	4.0E-3		IEC 60250
Comparative Tracking Index	150	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Glow Wire Flammability Index (2.00 mm)	960	°C	IEC 60695-2-12

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (400°C)	500	Pa·s	ISO 11443

Injection	Nominal Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	3.0 - 5.0	hr
Hopper Temperature	< 100	°C
Rear Temperature	360	°C
Middle Temperature	365	°C
Front Temperature	375	°C
Nozzle Temperature	380	°C
Mold Temperature	180 - 210	°C

Injection instructions
Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness

Note Message
1 .	Crystalline
2 .	Mold temperature: 190°C, melt temperature: 380°C
3 .	380°C nozzle

Resin Grade	Manufacturer	Category	Trademark
TECHNYL® A 258P1 BLACK 2N	Solvay Engineering Plastics	Nylon 66	TECHNYL® A
Trexprene® A55SCI	Mitsubishi Chemical Performance Polymers, Inc.	TPV	Trexprene®
Formolon® 676H	Formosa Plastics Corporation, U.S.A.	PVC Homopolymer	Formolon®
Hylon® N1220HL	Ravago Manufacturing Americas, LLC	Nylon 66	Hylon®
Hydrin® H1100	Zeon Chemicals L.P.	Epoxy	Hydrin®