Estaloc® 60204 RETPU
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estaloc® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v35c4e_Estaloc-60204-RETPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Type: Estaloc® 60204 Alloy is a Polyester-Type Reinforced Engineered Thermoplastic Polyurethane (RETPU). Features: Fast Cycling, Dimensional Stability, Durability, Aesthetics, Low Temperature Impact Uses: Injection Molding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow 1 | 0.060 | % | ASTM D955 |
| Flow 2 | 0.30 | % | ASTM D955 |
| Transverse flow 3 | 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 5 sec) | 71 - 77 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (0.762 mm) | 1900 | MPa | ASTM D638 |
| Tensile Strength (0.762 mm) | 32.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 0.762 mm) | 39 | % | ASTM D638 |
| Flexural Modulus (0.762 mm) | 1380 | MPa | ASTM D790 |
| Flexural Strength (0.762 mm) | 41.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 0.762 mm | 37 | J/m | ASTM D256 |
| 23°C, 0.762 mm | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 73.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 50.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 199 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 221 | °C | |
| Nozzle Temperature | 227 | °C | |
| Processing (Melt) Temp | 227 | °C | |
| Injection Pressure | 69.0 - 103 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 35.0 - 69.0 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Screw Speed | 30 - 80 | rpm |
| Injection instructions |
|---|
| Air Dew Point: -40°C |
| Note Message | |
|---|---|
| 1 . | Flex Bar |
| 2 . | Disc |
| 3 . | Disc |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 399 X 93608 | RTP Company | PC | RTP |
| Quadrant EPP Nylatron® GS | Quadrant Engineering Plastic Products | Nylon 66 | Quadrant EPP |
| TECHNYL® A 216 V30 NATURAL FA | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| MAJ'ECO DEN060LA | AD majoris | Biodeg Polymers | MAJ'ECO |
| LNP™ LUBRICOMP™ DBL349E compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |