| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Ghaed Basir Petrochemicals Co. |
| Trademark: | Ghaed ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v34AmC_Ghaed-ABS-ABS-70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Classification: General purpose Characteristic: Super High Impact Resistance Characteristic: Automobile parts(radiator grill &etc.),Helmets,Toys,Suitcase,Profiles Released extruded product ,Bobbin sleeve, Boats, pipe, bath tubs&etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 8.0 - 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 - 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 23°C) | > 43.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C) | > 18 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | > 1960 | MPa | ASTM D790 |
| Flexural Strength 4(23°C) | > 63.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 5 | > 23 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | > 96.0 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 190 - 200 | °C | |
| Middle Temperature | 200 - 220 | °C | |
| Front Temperature | 225 - 245 | °C | |
| Nozzle Temperature | 225 - 235 | °C | |
| Processing (Melt) Temp | 240 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Rate | Slow-Moderate |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 190 - 200 | °C | |
| Cylinder Zone 2 Temp. | 190 - 200 | °C | |
| Cylinder Zone 3 Temp. | 200 - 210 | °C | |
| Cylinder Zone 4 Temp. | 200 - 210 | °C | |
| Cylinder Zone 5 Temp. | 210 - 220 | °C | |
| Adapter Temperature | 210 - 220 | °C | |
| Die Temperature | 225 - 235 | °C |
| Extrusion instructions |
|---|
| Compression Ratio: 2.5:1 to 3:1L/D Ratio: 20:1Zone 6: 210 to 220°CZone 7: 210 to 220°CScreen Pack Mesh (2 layer): #60-80 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 6.4mm |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® H3KC(U) | BASF Leuna GmbH | Nylon 6 | Miramid® |
| Solarkote® P-611 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Solarkote® |
| ASACLEAN™ UB | ASACLEAN - Sun Plastech Inc. | Proprietary | ASACLEAN™ |
| Geon™ HTX M6307 | PolyOne Corporation | PVC Alloy | Geon™ HTX |
| POCAN® T 7391 POS151 900044 | LANXESS GmbH | PBT+PET | POCAN® |