Order Products : sales@su-jiao.com
RapidCast™ RC-542
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | RapidCast™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v2L8HI_RapidCast-RC-542.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RC-542 is a flame retardant elastomer formulated for room temperature meter-mix dispensing systems and short mold cycle times. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. RC-542 conforms to UL94vO flame resistance and is yellow card certified. RC-542 exhibits a very low viscosity, allowing for better mold-flow. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.07 | g/cm³ | |
| Cured | 1.14 | g/cm³ | |
| Base Resin | 1.26 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1590 | MPa | ASTM D790 |
| Flexural Strength | 60.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 89.0 | °C | |
| 1.8 MPa, Unannealed | 80.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 36 Mix Ratio by Weight: 31 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 10 to 20 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.10 | Pa·s | |
| 25°C 2 | 0.50 | Pa·s | |
| 25°C 3 | 1.8 | Pa·s | |
| Curing Time (25°C) | 24 | hr | |
| Gel Time | 0.50 to 0.83 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 70 to 80 | ASTM D2240 | |
| Tensile Strength | 38.6 | MPa | ASTM D638 |
| Tensile Elongation at Break | 11 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA U407 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| SLOVAMID® 66 GF 40 E/2M | Plastcom | Nylon 66 | SLOVAMID® 66 |
| NEXUS PP CPP1NB | Nexus Resin Group, LLC. | PP Impact Copolymer | NEXUS PP |
| Celazole® (U-Series) U-60SD | PBI Performance Products, Inc. | PBI | Celazole® (U-Series) |
| KumhoSunny ASA XC220 | Shanghai KumhoSunny Plastics Co., Ltd. | ASA | KumhoSunny ASA |