LAMIGAMID® 200
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Schwartz Technical Plastic |
| Trademark: | LAMIGAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v29k4w_LAMIGAMID-200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications:
|
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.15 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 2.5 - 3.0 | -- | % | ISO 62 |
| Saturated, 23°C | 7.5 - 9.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 170 | 100 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3300 | 2000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield | 90.0 | 60.0 | MPa | ISO 527-2 |
| Fracture | 135 | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 40 | > 150 | % | ISO 527-2 |
| Flexural Modulus | 2900 | 2000 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D1894 | |||
| With steel-dynamic | 0.020 | 0.080 | ASTM D1894 | |
| With steel-static | 0.35 | 0.42 | ASTM D1894 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | > 3.0 | > 15 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | No Break | No Break | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 105 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 255 | -- | °C | ISO 3146 |
| CLTE - Flow (20 to 100°C) | 7.0E-5 - 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1670 | -- | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.20 | -- | W/m/K | ISO 8302 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Dielectric Strength | 50 | 40 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.60 | 5.00 | IEC 60250 | |
| Dissipation Factor | 0.026 | 0.20 | IEC 60250 |
| Additional Information |
|---|
| 干燥 Creep Rate Stress, DIN 53444, 1% Elongation: >8 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: >12 N/mm²Friction Wear: 0.09 µm/KmPenetration Resistance, DIN 53482: 1E15 ohm-cmCreepage/leakage Resistance: KA3cThermal Expension: 0.1 %/10°CSafe Temperature Range, short periods: 170°CSafe Temperature Range, permanent: -30°C |
| 调节后的 Creep Rate Stress, DIN 53444, 1% Elongation: >8 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: >12 N/mm²Friction Wear: 0.09 µm/KmPenetration Resistance, DIN 53482: 1E12 ohm-cmCreepage/leakage Resistance: KA3bThermal Expension: 0.1 %/10°CSafe Temperature Range, short periods: 170°CSafe Temperature Range, permanent: 120°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil R-2380 | NuSil Technology | Silicone | NuSil |
| Axiall PVC 4510 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Durethan® BG 30 X H2.0 901510 | LANXESS GmbH | Nylon 6 | Durethan® |
| DURANEX® 310NF | Polyplastics Co., Ltd. | PBT | DURANEX® |
| Elastollan® 1195A10R | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |