Menzolit® BMC 0400
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v1Lq7T_Menzolit-BMC-0400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® BMC 0400 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens nor any heavy metals. Menzolit® BMC 0400 is a low profile DMC/BMC for automotive applications. It fulfils the requirements of the automotive industry regarding painted body panels including reduced C-emissions. For highest surface quality we recommend processing on mirror finish chrome-plated steel moulds. The material shows a high thermal resistance for on-line painting at 190- 200 °C. Adhesion of paint is excellent. The material doesn't shrink during moulding, it even expands. Therefore warpage is reduced and dimensional stability is excellent. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.90 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- 1 | 0.0 | % | DIN 53464 |
| -- | -0.050 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 14000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 36.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Compression Molded) | 1.0 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 11000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 120 | MPa | ISO 178 |
| Poisson's Ratio | 0.30 | Internal Method | |
| Matrix Crazing Strain | 0.30 | % | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 30 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 150 | °C | ISO 75-2/A |
| Continuous Use Temperature | 170 | °C | Internal Method |
| Glass Transition Temperature | 170 | °C | DSC |
| CLTE - Flow | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 135 to 160 | °C | |
| Injection Pressure | 2.00 to 8.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime 2400 | Prime PVC® | PVC, Rigid | Prime |
| SCHULAMID® 6 GF 30 FR2 A LM WEISS 96.0342 LM | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| TEKNIFLEX® VAV54005 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PCTFE/PVC | TEKNIFLEX® |
| Starex HP-0500 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Dryflex® 422401S | ELASTO | SBS | Dryflex® |