MELOPAS® MF 3025
| Category: | Mel Formald , Melamine Formaldehyde |
| Manufacturer: | RASCHIG GmbH |
| Trademark: | MELOPAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v15gs0_MELOPAS-MF-3025.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cellulose reinforced Melamine moulding compound Exceptional surface hardness, good UV-stability and heat resistance, very good resistance to chemicals, especially foodstuffs and their additives Primary application(s): Pot and pan handles This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 to 1.80 | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 to 0.80 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow | ISO 2577 | ||
| -- 1 | 0.50 to 1.0 | % | |
| -- 2 | 0.80 to 1.2 | % | |
| Water Absorption (23°C, 24 hr) | < 2.0 | % | ISO 62 |
| Post Shrinkage 3 | 1.0 to 1.5 | % | ISO 2577 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature | IEC 60216 | ||
| <50 h | 170 | °C | |
| 20,000 h | 140 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 20.0 | MPa | |
| Compression Molding Temperature | 160 to 180 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| Compression Molded | 5000 to 8000 | MPa | |
| Injection Molded | 5000 to 8000 | MPa | |
| Tensile Stress | ISO 527-2 | ||
| Compression Molded | 45.0 to 65.0 | MPa | |
| Injection Molded | 50.0 to 90.0 | MPa | |
| Flexural Modulus | ISO 178 | ||
| Compression Molded | 7000 to 9000 | MPa | |
| Injection Molded | 7000 to 9000 | MPa | |
| Flexural Stress | ISO 178 | ||
| Compression Molded | 80.0 to 100 | MPa | |
| Injection Molded | 110 to 130 | MPa | |
| Compressive Stress | 200 to 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| Compression Molded | 1.8 to 2.2 | kJ/m² | |
| Injection Molded | 1.8 to 2.2 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| Compression Molded | 7.0 to 9.0 | kJ/m² | |
| Injection Molded | 8.0 to 14 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 160 to 180 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 120 to 140 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 100°C) | 1.5E-5 to 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.40 to 0.50 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+11 to 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 15 to 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 16.0 11.0 | ||
| 1 MHz | 9.00 7.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.30 to 0.50 | ||
| 1 MHz | 0.030 to 0.050 | ||
| Arc Resistance | PLC 5 | ASTM D495 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Tested by RASCHIG) | V-0 | UL 94 | |
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 900 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Middle Temperature | 70.0 to 90.0 | °C | |
| Front Temperature | 90.0 to 100 | °C | |
| Processing (Melt) Temp | 100 to 115 | °C | |
| Mold Temperature | 160 to 180 | °C | |
| Back Pressure | 0.800 to 1.20 | MPa | |
| Screw Speed | 80 to 120 | rpm |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | Injection Molded |
| 3 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRILOY AC3250 | Formosa Plastics Corporation | PC+ABS | TAIRILOY |
| AKROMID® T1 GF 60 black (3419) | AKRO-PLASTIC GmbH | PPA | AKROMID® |
| KOPA® KN333G35CRBK | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Lupolen 2421 F | LyondellBasell Industries | LDPE | Lupolen |
| Lushan VB150A | Guangzhou Lushan New Materials Co., Ltd | PE, Unspecified | Lushan |