Modified Plastics MN 6/6-FG 10
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Modified Plastics, Inc. |
| Trademark: | Modified Plastics |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uzcTbK_Modified-Plastics-MN-6-6-FG-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified Plastics MN 6/6-FG 10 is a Polyamide 66 (Nylon 66) product filled with 10% glass fiber. It can be processed by injection molding and is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.7 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 1.3 | % | |
| Saturation | 7.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 89.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 4550 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 138 | MPa | ASTM D790 |
| Compressive Strength | 117 | MPa | ASTM D695 |
| Shear Strength | 62.1 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 6.35 mm) | 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 257 | °C | |
| 1.8 MPa, Unannealed | 249 | °C | |
| Vicat Softening Temperature | 265 | °C | ASTM D1525 |
| CLTE - Flow | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 4.10 | ||
| 1 kHz | 1.90 | ||
| 1 MHz | 3.70 | ||
| Dissipation Factor (1 kHz) | 0.030 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 93.3 to 104 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene RCC220-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| AQUATUF® HMP-337 (Roto) | Ravago Manufacturing Americas, LLC | HDPE | AQUATUF® |
| Dugdale PVC Rigid Extrusion - Water White Compound | Dugdale Plc | PVC, Rigid | Dugdale PVC |
| Grilon® TSGL-60/4 black 9833 | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| Karina GREEN PVC COMPOUND 852-40/5-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |