Lupoy® HI5002A
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uzTaXq_Lupoy-HI5002A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupoy® HI5002A is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Lupoy® HI5002A are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 54.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 70 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2060 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 84.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 560 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Minimum Moisture Content | 0.020 | % | |
| Rear Temperature | 230 to 255 | °C | |
| Middle Temperature | 235 to 265 | °C | |
| Front Temperature | 235 to 265 | °C | |
| Nozzle Temperature | 235 to 265 | °C | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Veroplas VGR10 | PlastxWorld Inc. | ABS | Veroplas |
| Toyolac® SX10G-15 | Toray Resin Company | Nylon 6+ABS | Toyolac® |
| Zytel® LC6601 BK551 | DuPont Performance Polymers | Nylon 612 | Zytel® |
| Niplene T40 | Soredi S.p.a. | PP Homopolymer | Niplene |
| ICORENE® 9035 | ICO Polymers APAC, A Division of A. Schulman | LMDPE | ICORENE® |