K-Resin® SBC KR01
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | K-Resin® SBC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uwFtM1_K-Resin-SBC-KR01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
K-Resin® SBC KR01 is a Styrene Butadiene Block Copolymer (SBC) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding, profile extrusion, or thermoforming. Important attributes of K-Resin® SBC KR01 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 69 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 33.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 30 | % | ASTM D638 |
| Flexural Modulus 3(3.18 mm) | 1800 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.18 mm) | 54.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact 5(23°C, 3.18 mm) | 2.15 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 64.4 | °C | ASTM D648 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (60°) | 164 | ASTM D523 | |
| Transmittance | 93.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 193 to 232 | °C | |
| Mold Temperature | 10.0 to 48.9 | °C | |
| Back Pressure | 0.345 to 1.03 | MPa | |
| Clamp Tonnage | 2.8 to 8.3 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | 13 mm/min |
| 4 . | 13 mm/min |
| 5 . | 3.81 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-5342-9000 | Ravago Manufacturing Americas, LLC | PP Homopolymer | Ravago Compounds |
| Bergamid™ A70 G10 H BK032 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Fortron® 1140L7 | Celanese Corporation | PPS | Fortron® |
| HIVAL® 2435 | Nexeo Solutions, LLC. | PP Homopolymer | HIVAL® |
| LNP™ STAT-KON™ DX04490 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |