KumhoSunny PC/ABS HAC5010G
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PC/ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uw9Awg_KumhoSunny-PC-ABS-HAC5010G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HAC5010G is a good dimensional stability glass fiber reinforced PC/ABS resin . |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow | 0.30 to 0.50 | % | ASTM D955 |
| -- | 0.30 to 0.50 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 70.0 | MPa | ASTM D638 |
| -- | 65.0 | MPa | ISO 527-2/5 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 4000 | MPa | ASTM D790 |
| -- 1 | 3500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 110 | MPa | ASTM D790 |
| -- 2 | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 10 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 3.20 mm | 130 | J/m | ASTM D256 |
| 23°C 4 | 9.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 112 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 122 | °C | ASTM D1525 6 |
| -- | 120 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 240 to 260 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 250 to 260 | °C | |
| Processing (Melt) Temp | 260 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 0.300 to 1.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 4J |
| 4 . | 5.5J |
| 5 . | 120°C/h |
| 6 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravaflex EPM P | Ravago Group | EPM | Ravaflex |
| SOLARENE DM500 | Dongbu Hannong Chemical | PS (GPPS) | SOLARENE |
| Axiall PVC 19740 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Karina RED COLOR CONCENTRATE -E 42/183-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Mediprene® 500652M | ELASTO | SEBS | Mediprene® |