EL-Pro™ P602F
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Pro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uw2cgO_EL-Pro-P602F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-PRO P600F is a Homopolymer polypropylene resin without slip and antiblock agent. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1670 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 25 µm | 686 | MPa | |
| 2% Secant, TD : 25 µm | 539 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 28.4 | MPa | |
| TD : Yield, 25 µm | 19.6 | MPa | |
| MD : Break, 25 µm | 27.5 | MPa | |
| TD : Break, 25 µm | 25.5 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 850 | % | |
| TD : Break, 25 µm | 770 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 25 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Brittleness Temperature | < -10.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 155 | °C | ASTM D1525 |
| Melting Temperature | 160 | °C | ASTM D2117 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 75 | ASTM D2457 | |
| Haze | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Baydur® 684 (25 pcf) | Covestro - PUR | PUR, Unspecified | Baydur® |
| Fainplast PVC RH 212/W | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| DOWLEX™ 2037 | The Dow Chemical Company | LLDPE | DOWLEX™ |
| FRblend® PBT-1304 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PBT | FRblend® |
| KOPLA PA66 KDG1030F | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |