Crastin® ST830FRUV NC010
| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Crastin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uvtgnF_CrastinST830FRUVNC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced, Flame Retardant, UV Stabilized, Polybutylene Terephthalate |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.6 | % | ISO 294-4 |
| Flow | 2.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 41.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 45 | % | ISO 527-2 |
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 10 | kJ/m² | ISO 179/1eA |
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 65 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C | 350 | kJ/m² | ISO 179/1eU |
| -30°C | 350 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | 10 | kJ/m² | ISO 180/1A |
| -30°C | 10 | kJ/m² | ISO 180/1A |
| 23°C | 70 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -40°C | 220 | kJ/m² | ISO 180/1U |
| -30°C | 220 | kJ/m² | ISO 180/1U |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 125 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.9E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.9E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 36 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.50 | IEC 60250 | |
| 1 MHz | 3.40 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.1E-3 | IEC 60250 | |
| 1 MHz | 0.024 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.9 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| Oxygen Index | 27 | % | ISO 4589-2 |
| FMVSS Flammability | DNI | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 250 | °C | |
| Mold Temperature, Optimum | 80 | °C | |
| Back Pressure | As low as possible | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.17 | g/cm³ | |
| Ejection Temperature | 170 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 30 - 130 | °C | |
| Holding Pressure | 60.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2802-40D | RTP Company | TPO (POE) | RTP |
| ACCUTECH™ CP0437M10CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Hapcoat™ 3727 | Hapco Inc. | TP, Unspecified | Hapcoat™ |
| Sylvin 5224-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Hifax TYC 1152X BLACK | LyondellBasell Industries | TPO (POE) | Hifax |