Petrothene® NA336
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uvkkas_Petrothene-NA336.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene NA336 is a series of homopolymer resins selected by customers for applications that require thin gauge film constructions. NA336 resins are known for their consistency, excellent drawdown and processability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 32 µm, blown film | 146 | MPa | ASTM D882 |
| 1% secant, TD : 32 µm, blown film | 165 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm, blown film | 17.2 | MPa | ASTM D882 |
| TD : Yield, 32 µm, blown film | 13.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 230 | % | ASTM D882 |
| TD : Broken, 32 µm, blown film | 450 | % | ASTM D882 |
| Dart Drop Impact (32 µm, Blown Film) | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm, blown film | 350 | g | ASTM D1922 |
| TD : 32 µm, blown film | 150 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 31.8 µm, Blown Film) | 62 | ASTM D2457 | |
| Haze (31.8 µm, Blown Film) | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 149 - 166 | °C |
| Extrusion instructions |
|---|
| NA 336 has been specifically designed to provide outstanding drawdown at maximum outputs. The melt strength properties of this resin result in excellent bubble stability. This resin can be processed over a wide range of temperatures; however, recommended conditions are melt temperatures between 300°- 330°F (149°-166°C) and a blow-up ratio between 2.0-2.5:1. Using proper techniques and equipment, drawdown to 0.25 mil (6 microns) is feasible at commercial production rates. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| StarGRIP GP 30-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarGRIP |
| Tarnoform® 300 TF05 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Tritan™ TX2001 | Eastman Chemical Company | Copolyester | Tritan™ |
| apilon 52® 6013 | API SpA | TPU-Polyester | apilon 52® |
| CompaDur® 121 GF 30 black (027) | DimeLika Plast GmbH | PBT | CompaDur® |