| Vydyne 49 is general-purpose, impact-modified PA66 resin. Available in natural, it is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.11 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 2.00 mm | 1.6 | -- | % | |
| Flow : 2.00 mm | 1.8 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.3 | -- | % | |
| Equilibrium, 50% RH | 2.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3040 | 2130 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield | 70.0 | 50.0 | MPa | |
| Break | 46.0 | 42.0 | MPa | |
| Tensile Strain (Break) | 17 | 40 | % | ISO 527-2 |
| Flexural Modulus | 2600 | 890 | MPa | ISO 178 |
| Flexural Stress | 81.0 | 27.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 8.0 | 6.0 | kJ/m² | |
| -30°C | 11 | 10 | kJ/m² | |
| 23°C | 13 | 43 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180 | |||
| -40°C | 8.0 | 10 | kJ/m² | |
| -30°C | 9.0 | 15 | kJ/m² | |
| 23°C | 10 | 37 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 202 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 69.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00 mm | 8.6E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 1.2E-4 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 125 | -- | °C | |
| 1.50 mm | 125 | -- | °C | |
| 3.00 mm | 125 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 75.0 | -- | °C | |
| 1.50 mm | 75.0 | -- | °C | |
| 3.00 mm | 75.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 85.0 | -- | °C | |
| 1.50 mm | 85.0 | -- | °C | |
| 3.00 mm | 85.0 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (0.750 mm) | 1.0E+12 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 23 | -- | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | PLC 5 | -- | ASTM D495 | |
| Comparative Tracking Index (3.00 mm) | 600 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.750 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | -- | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.750 mm | PLC 4 | -- | ||
| 1.50 mm | PLC 4 | -- | ||
| 3.00 mm | PLC 3 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.750 mm | 700 | -- | °C | |
| 1.50 mm | 750 | -- | °C | |
| 3.00 mm | 700 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.750 mm | 725 | -- | °C | |
| 1.50 mm | 775 | -- | °C | |
| 3.00 mm | 725 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Automotive Materials - (thickness d = 1 mm) | + | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene G30P100-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| SuperLite® SL550800-100 (3.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Sumitomo Epoxy TEM 9053C | Sumitomo Bakelite North America, Inc. | Epoxy | Sumitomo Epoxy |
| Hostacom X M2 U34 102942 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Infino LX-1080 | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |