Order Products : sales@su-jiao.com
INEOS HDPE J60-800-178
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uvPYVt_INEOS-HDPE-J60-800-178.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| J60-800-178 is a high density polyethylene homopolymer intended for the injection molding of beverage closures. Because of its excellent organoleptic properties, this grade is certified as low taste and is intended for use in direct contact with beverages. Parts fabricated from this material exhibit a glossy surface finish and have good impact strength and rigidity. Typical applications include caps and closures for the packaging of still and sparkling water and other injection molded applications where low taste and odor are critical. This material meets the Food and Drug Administration requirements of 21 CFR 177.1520. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.961 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.9 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, F50) | 4.00 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 31.4 | MPa | |
| Break | 15.8 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 8.3 | % | |
| Break | 940 | % | |
| Flexural Modulus - Tangent | 1650 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 38 | J/m | ASTM D256 |
| Notched Izod Impact (Area) | 3.75 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 78.9 | °C | ASTM D648 |
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® PM-9630K | Sumitomo Bakelite Co., Ltd. | Phenolic | Sumikon® |
| STYRON™ 686E | Trinseo | PS (GPPS) | STYRON™ |
| Ultradur® B 4300 G6 High Speed | BASF Corporation | PBT | Ultradur® |
| Baydur® STR/C-1000 | Covestro - PUR | PUR-MDI | Baydur® |
| Cevian®-N 070SF | Daicel Polymer Ltd. | SAN | Cevian®-N |