OMIKRON KLS 70 NERO
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TECNOPOL |
| Trademark: | OMIKRON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uvMkS4_OMIKRON-KLS-70-NERO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP COPOLYMER, 30% TALCUM, BLACK |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 17 | % | ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 4.0 | kJ/m² | ISO 180 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Aging (150°C) | > 6.3 | day | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 66.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 70.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 220 - 250 | °C | |
| Middle Temperature | 220 - 250 | °C | |
| Front Temperature | 220 - 250 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Pressure | 90.0 - 110 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 5.00 - 10.0 | MPa |
| Injection instructions |
|---|
| Post Pressure: 60 - 80 bar |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitarex® 616 | Taita Chemical Company, Ltd. | PS (HIPS) | Taitarex® |
| TEREZ PC/ASA Blend 2002 | TER HELL PLASTIC GMBH | ASA+PC | TEREZ PC/ASA |
| NEXT SIGNATURE POMC HF-300 | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT SIGNATURE |
| ColorFast® PCGF130 | LTL Color Compounders, Inc. | PC | ColorFast® |
| LNP™ LUBRICOMP™ WFL34H compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |