Akulon® XG-FKGS6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uuwAVf_Akulon-XG-FKGS6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon® XG-FKGS6 is a Polyamide 6 (Nylon 6) material filled with 30% glass fiber. It is available in Asia Pacific or Europe. Important attributes of Akulon® XG-FKGS6 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.7 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11500 | 7100 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 135 | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 3.7 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.800 mm | V-0 | -- | ||
| 1.60 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.00 mm | 775 | -- | °C | |
| 1.60 mm | 775 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 230 to 260 | °C | |
| Front Temperature | 230 to 260 | °C | |
| Nozzle Temperature | 250 to 280 | °C | |
| Processing (Melt) Temp | 245 to 270 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF4BTL (Series: FC/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Wellamid® GF33A099-HRN | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Kingfa FRHIPS-980 | Kingfa | PS (HIPS) | Kingfa |
| Karina IVORY PVC COMPOUND -E 809D35/ 1-CY-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 7844-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |