ACLAR® 22A (1.5 mil)
| Category: | PCTFE , Polychlorotrifluoroethylene |
| Manufacturer: | Honeywell |
| Trademark: | ACLAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uuNdMB_ACLAR-22A-1-5-mil-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aclar 22A is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It is a flexible transparent film used to package moisture sensitive products. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.08 | g/cm³ | ASTM D1505 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD : 38 µm | 1030 | MPa | ASTM D882 |
| TD : 38 µm | 1070 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm | 64.1 | MPa | ASTM D882 |
| TD : Yield, 38 µm | 44.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 38 µm | 170 | % | ASTM D882 |
| TD : Yield, 38 µm | 250 | % | ASTM D882 |
| Water Vapor Transmission Rate (38 µm, 38°C, 100% RH) | 0.34 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 190 | °C | ASTM D3418 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (0.0381 mm) | 100 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (38.1 µm) | < 1.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield, No Standard: 12.64 m²/kgTear Strength, ASTM D1004, Graves MD: 325 to 350 g/milTear Strength, ASTM D1004, Graves TD: 250 to 325 g/milCrystalline Melting Point, ASTM D4591: 190 °CDimensional Stability, ASTM D1204, MD: +12 to +15 %Dimensional Stability, ASTM D1204, TD: -12 to -15 %Tensile Strength @ yld, ASTM D882, MD: 7500 to 11000 psiTensile Strength @ yld, ASTM D882, TD: 5000 to 8000 psiElongation @ Yield, ASTM D882, MD: 115 to 225%Elongation @ Yield, ASTM D882, TD: 200 to 300%Secant Modulus, ASTM D882, MD: 140000 to 160000 psiSecant Modulus, ASTM D882, TD: 150000 to 160000 psiFlammability: non-flammable |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefanyl® VR VRGR 321 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | tefanyl® VR |
| Boltaron 9230 | Boltaron Performance Products | PVC, Unspecified | Boltaron |
| Axpoly® PP19 1021 | Axion Polymers | PP Homopolymer | Axpoly® |
| OmniTech™ PBT GR30 | OMNI Plastics, LLC | PBT | OmniTech™ |
| Polifil® PP GFPPCC-40 | The Plastics Group | PP Homopolymer | Polifil® PP |