SABIC® LLDPE 318B

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	Saudi Basic Industries Corporation (SABIC)
Trademark:	SABIC® LLDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	usHf0w_SABIC-LLDPE-318B.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

SABIC® LLDPE 318B is a butene linear low density polyethylene resin typically designed for easy processing and specially formulated for optimum thermal stability at high temperatures used in cast film extrusion. Cast film produced from SABIC® LLDPE 318B exhibit very good optical properties, puncture resistance and tear strength.

Application

Cast Film: SABIC® LLDPE 318B resin is typcially used for hand and pallet stretch wrap.

Masterbatch Compounding: SABIC® LLDPE 318B is a general grade, typically used for low filled or additive masterbatches in film and blow moulding applications (e.g. slip agents, anti fog agents, anti static agents, thermal stabilizers).

This product is not intended for and must not be used in any pharmaceutical/medical applications.

General Information
Additive	Antioxidation
Features	Low density Butene comonomer Optical Perforation resistance Antioxidation Workability, good Good tear strength Low liquidity Thermal stability, good
Uses	Composite Stretch winding cast film Masterbatch
Processing Method	Composite cast film

Physical	Nominal Value	Unit	Test Method
Density	0.918	g/cm³	ISO 1183/A
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.8	g/10 min	ISO 1133

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	20	µm
Elastic Recovery - Cast Film (20.0 µm)	52	%	ASTM D5459
Protrusion Puncture Resistance - Cast Film (20.0 µm)	2.00	J	ASTM D5748
Stress Retention - Cast Film (20.0 µm)	78	%	ASTM D5459

Thermal	Nominal Value	Unit	Test Method
Enthalpy Change	114	J/g	Internal method

Additional Information	Nominal Value	Unit	Test Method
Dart Impact - Cast Film (20.0 µm)	26.0	J/cm	ISO 7765-2
Tear Strength - TD ¹(20.0 µm)	140.0	kN/m	ISO 6383-2

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	102	°C	ISO 306/A
Melting Temperature (DSC)	121	°C	Internal method

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 20.0 µm, Cast Film)	91		ASTM D2457
Haze (20.0 µm, Cast Film)	2.1	%	ASTM D1003

Additional Information	Nominal Value	Unit	Test Method
Properties are determined on 20 µm cast stretch film produced on a 2 m commercial cast stretch line: melt temperature 270°C, chill roll temperature 20°C and line speed of 450 m/min.

Extrusion	Nominal Value	Unit
Melt Temperature	250 - 300	°C

Note Message
1 .	Cast Film

Resin Grade	Manufacturer	Category	Trademark
Ming Dih EPS LS3	Ming Dih Group Corporation	PS (EPS)	Ming Dih EPS
Witcom PPS 6C/3L1-L	Witcom Engineering Plastics B.V.	PPS	Witcom PPS
Flontech® FT-GL25-NPA-6	Guarniflon S.p.A. - Flontech Division	PTFE	Flontech®
KMI PP KM-Y093R	KMI Group, Inc.	PP Random Copolymer	KMI PP
Sylvin 9925-85 BLACK	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin