AKROMID® A3 5 black (4701)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | urEg5f_AKROMID-A3-5-black-4701-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 5 black (4701) is an unreinforced, high temperature stabilised polyamide 6.6 Applications are housings and fixtures in the automotive and electric industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.14 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 127 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.5 | -- | % | |
| Flow | 1.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3500 | 1450 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 90.0 | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 4.5 | -- | % | |
| Break | 12 | > 30 | % | |
| Flexural Modulus 1 | 3200 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 125 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 260 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | V-2 | -- | UL 94 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 2.0 | -- | % | ISO 1172 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 1018 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| QR Resin QR-1220 | QTR, Inc. | PC+ABS | QR Resin |
| Asaprene™ T-432 | AKelastomers | SBS | Asaprene™ |
| Formolene® LH5214 | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |
| Ecomann® Bioresin EM30010 | Shenzhen Ecomann Biotechnology Co., Ltd. | PHA | Ecomann® |