INNOPOL® PP CS 1-3130 MA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ur9Zrc_INNOPOL-PP-CS-1-3130-MA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL CS 1-3130 MA is a 30 % talcum filled compound based on polypropylene homopolymer. This grade is available in nature and custom coloured form. Recommended application INNOPOL® CS 1-3130 MA is recommended especially for producing products, where high stiffness, low shrinkage and long term heat stability required. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.6 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 2.1 | kJ/m² | ISO 179/1eA |
| 23°C | 2.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 14 | kJ/m² | ISO 179/1eU |
| 23°C | 27 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 123 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 67.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A120 |
| -- | 92.0 | °C | ISO 306/B120 |
| Melting Temperature | 164 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| flammability- Automotive materials (thickness d > 1 mm) | + | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 250 | °C | |
| Middle Temperature | 190 - 250 | °C | |
| Front Temperature | 190 - 250 | °C | |
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 20.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold pressure: 30-100% of injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9018 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| DOMAMID® 6G20GT96M | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| Geon™ Vinyl Fittings 216A | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Fittings |
| ELASTOSIL® R 420/70 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| PETLIN LD M022X | PETLIN (MALAYSIA) SDN BHD | LDPE | PETLIN |