Geon™ Vinyl Rigid Extrusion L4794
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Rigid Extrusion |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uqdpzi_Geon-Vinyl-Rigid-Extrusion-L4794.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon L4794 is currently recommended for non-horizontal dark color outdoor profile applications only due to limited data. Exhibits comparable processing to previous Geon L1534 and 85885 type products. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 1-22431-33 | ASTM D4216 | |
| PVC Cell Classification | 13334 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 77 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2260 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 43.9 | MPa | ASTM D638 |
| Flexural Modulus | 2490 | MPa | ASTM D790 |
| Flexural Strength | 76.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 100 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 72.5 | J/cm | ASTM D4226 |
| 23°C 4 | > 178 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, annealed, 3.18mm 5 | 73.1 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm 6 | 71.0 | °C | ASTM D648 |
| 1.8 MPa, annealed 7 | 69.3 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm 8 | 69.8 | °C | ASTM D648 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Acceptable | ||
| 注释：物理属性基于L7005 tan 3210 样品。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Procedure A, C.125 Throwing |
| 4 . | Procedure B, C.125 Throwing |
| 5 . | Annealed at 60 deg.C |
| 6 . | Conditioned at 50 deg.C |
| 7 . | Annealed at 50 deg.C |
| 8 . | Annealed at 60 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV X23080N | Teknor Apex Company | TPV | Sarlink® TPV |
| SCANAMID 66 A43^E F14 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Argyle ABSmax (P430) | Argyle Materials Inc. | ABS | Argyle |
| KYOCERA KE-G3400 | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| Durethan® AKV 35 H3.0 000000 | LANXESS Asia/Pacific | Nylon 66 | Durethan® |