CALIBRE™ MEGARAD™ 2081-15

Category: PC , Polycarbonate Resin
Manufacturer: Trinseo
Trademark: CALIBRE™
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: uqFLMv_CALIBRE-MEGARAD-2081-15.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
CALIBRE™ MEGARAD 2081-15 Polycarbonate resin provides end-users of radiation sterilized medical devices a color closer to the water-clear look of the natural resin. When exposed to high energy radiation (gamma or electron beam), CALIBRE MEGARAD 2081-15 resin can reduce the color shift by 50% compared to general purpose polycarbonate resins. CALIBRE 2081-15 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications.

Main Characteristics:
  • Stabilized for higher engery radiation
  • Tested under ISO 10993
  • Transparent
  • Contains mold release

Applications:
  • Medical applications
General Information
Additive
  • Mold Release
Features
  • Biocompatible
Uses
  • Electrical/Electronic Applications
  • General Purpose
  • Medical/Healthcare Applications
Agency Ratings
  • ISO 10993 2
Appearance
  • Clear/Transparent
Forms
  • Pellets
Processing Method
  • Injection Molding
Multi-Point Data
  • Specific Heat vs. Temperature (ASTM D3417)
  • Specific Volume vs Temperature (ISO 11403-2)
  • Tensile Stress vs. Strain (ASTM D638)
  • Thermal Conductivity vs. Temperature (ASTM E1530)
  • Viscosity vs. Shear Rate (ASTM D3835)
PhysicalNominal ValueUnitTest Method
Specific Gravity
    -- 1.20g/cm³ASTM D792, ISO 1183/A
    -- 1200kg/m³ISO 1183 1
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)15g/10 minASTM D1238, ISO 1133
Melt volume-flow rate (300°C/1.2 kg)12.0cm³/10minISO 1133 2
Molding Shrinkage - Flow 0.50 to 0.70%ASTM D955, ISO 294-4
Water Absorption ASTM D570, ISO 62
    23°C, 24 hr 0.15%
    Equilibrium, 23°C, 50% RH 0.32%
HardnessNominal ValueUnitTest Method
Rockwell Hardness (R-Scale)118ASTM D785
MechanicalNominal ValueUnitTest Method
Tensile Modulus
    -- 32210MPaASTM D638
    -- 2300MPaISO 527-2/50, ISO 527-2 4
Tensile Strength
    Yield 562.1MPaASTM D638
    Yield 62.0MPaISO 527-2/50, ISO 527-2 6
    Break 768.3MPaASTM D638
    Break 68.0MPaISO 527-2/50
Tensile Elongation
    Yield 86.0%ASTM D638
    Yield 6.0%ISO 527-2/50, ISO 527-2 9
    Break 10150%ASTM D638
    Break 150%ISO 527-2/50
Nominal strain at break > 50%ISO 527-2 11
Flexural Modulus
    -- 122410MPaASTM D790
    -- 2400MPaISO 178
Flexural Strength
    -- 1396.5MPaASTM D790
    -- 98.0MPaISO 178
Taber Abrasion Resistance 45%ASTM D1044
ImpactNominal ValueUnitTest Method
Charpy Notched Impact Strength
    23°C 25kJ/m²ISO 179/1eA
    -30°C 12.0kJ/m²ISO 179/1eA 14
    23°C 80.0kJ/m²ISO 179/1eA 15
Charpy impact strength ISO 179/1eU 16
    -30°C No Break
    23°C No Break
Notched Izod Impact
    23°C 750J/mASTM D256
    23°C 75kJ/m²ISO 180/A
Unnotched Izod Impact (23°C)No BreakASTM D256, ISO 180
Instrumented Dart Impact 17(23°C, Total Energy)81.3JASTM D3763
Tensile Impact Strength 378kJ/m²ASTM D1822
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load
    0.45 MPa, Annealed 139°CASTM D648
    0.45 MPa 137°CISO 75-2 18
    1.8 MPa, Unannealed 122°CASTM D648
    1.8 MPa, Unannealed 120°CISO 75-2/A
    1.8 MPa, Annealed 136°CASTM D648
    1.8 MPa 123°CISO 75-2 19
Vicat Softening Temperature
    -- 148°CASTM D1525 20
    -- 143°CISO 306/B50
    50°C/h, B (50N) 143°CISO 306 21
CLTE - Flow
    -40 to 82°C 6.8E-5cm/cm/°CASTM D696
    -- 7.0E-5cm/cm/°CISO 11359-2 22
ElectricalNominal ValueUnitTest Method
Volume Resistivity
    -- 2.0E+17ohms·cmASTM D257
    -- > 1.0E+13ohms·mIEC 60093 23
Dielectric Strength 17kV/mmASTM D149, IEC 60243-1 3 24
Dielectric Constant
    60 Hz 3.00ASTM D150
    1 MHz 3.00ASTM D150, IEC 60250 25
    100 Hz 3.00IEC 60250 26
Dissipation Factor
    50 Hz 1.0E-3ASTM D150
    1 MHz 2.0E-3ASTM D150, IEC 60250 27
    100 Hz 1.0E-3IEC 60250 28
FlammabilityNominal ValueUnitTest Method
Burning Behav. at 1.6mm nom. thickn. (1.60 mm, UL)HBISO 1210 29
Burning Behav. at thickness h (3.20 mm, UL)HBISO 1210 30
OpticalNominal ValueUnitTest Method
Refractive Index 1.586ASTM D542, ISO 489
Transmittance 85.0%ASTM D1003
Haze 1.0%ASTM D1003
Note Message
1 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
2 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
3 .50 mm/min
4 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
5 .50 mm/min
6 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
7 .50 mm/min
8 .50 mm/min
9 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
10 .50 mm/min
11 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
12 .Method I (3 point load), 2.0 mm/min
13 .Method I (3 point load), 2.0 mm/min
14 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
15 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
16 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
17 .3.39 m/sec
18 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
19 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
20 .Rate A (50°C/h), Loading 2 (50 N)
21 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
22 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
23 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
24 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
25 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
26 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
27 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
28 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
29 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
30 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
Resin Grade Manufacturer Category Trademark
Ren Ren Shape 450 Huntsman Advanced Materials PUR, Unspecified Ren
Sasol Polymers PP HMR040 Sasol Polymers PP Homopolymer Sasol Polymers PP
SUSTAGLIDE PLUS Röchling Sustaplast SE & Co. KG Nylon 6 SUSTAGLIDE
Jackdaw PP EX10BK6537 Jackdaw Polymers PP, Unspecified Jackdaw PP
Lucel® HI510 LG Chem Ltd. Acetal (POM) Copolymer Lucel®

TEL: +86-21-58958519 Email:sales@su-jiao.com

No. 215, Lianhe North Road, Fengxian District, Shanghai, China​， COPYRIGHT SUSHENG COMPANY RIGHTS RESERVED