Lastilac AR-V0E
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Lastilac |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uq1iob_Lastilac-AR-V0E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Acrylonitrile-Butadiene-Styrene copolymer (ABS) based compound. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Very high dimensional stability. Very good surface appearance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.45 to 0.65 | % | |
| Flow : 2.00 mm | 0.40 to 0.60 | % | |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 2300 | MPa | |
| 60°C | 1900 | MPa | |
| 90°C | 1500 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 40.0 | MPa | |
| Yield, 60°C | 30.0 | MPa | |
| Yield, 90°C | 20.0 | MPa | |
| Break, 23°C | 35.0 | MPa | |
| Break, 60°C | 20.0 | MPa | |
| Break, 90°C | 5.00 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 2.0 | % | |
| Yield, 60°C | 2.3 | % | |
| Yield, 90°C | 2.0 | % | |
| Break, 23°C | 8.0 | % | |
| Break, 60°C | 50 | % | |
| Break, 90°C | 95 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 4.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 35 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 85.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 70.0 | °C | |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 850 | °C | |
| 2.00 mm | 725 | °C | |
| Oxygen Index | 28 | % | ASTM D2863 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Dimensional Stability | 79.0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 15 | % | |
| Processing (Melt) Temp | 180 to 220 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bayflex® 190 RRIM (20% Mineral) | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| BITONER® BT-100 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| Hifax X M1 T11 356525 | LyondellBasell Industries | PP Copolymer | Hifax |
| Karina GREEN COLOR CONCENTRATE 40/447-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petrothene® LB010000 | LyondellBasell Industries | HDPE | Petrothene® |