PLUSTEK PD304G6YL55
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | upfEpp_PLUSTEK-PD304G6YL55.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GLASS FIBER REINFORCED POLYAMIDE 12 FOR INJECTION MOLDING APPLICATIONS. UL LISTED MATERIAL. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.20 - 0.30 | % | ASTM D955 |
| -- | 0.20 - 0.30 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 120 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 5200 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 160 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C | 15 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 177 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 165 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 165 - 175 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 215 - 255 | °C | |
| Middle Temperature | 220 - 260 | °C | |
| Front Temperature | 225 - 265 | °C | |
| Mold Temperature | 65.0 - 105 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa PP ZF-T30 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| DINALON® A1S25 G25 | Grupo Repol | Nylon 66 | DINALON® |
| EPO-TEK® E3037-LV | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Luranyl® KR 2462 G2 | ROMIRA GmbH | PPE+PS | Luranyl® |
| Durethan® C 38 FKS 000000 | LANXESS Corporation | Nylon 6 | Durethan® |