Starex TF-0956
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | unYbd1_Starex-TF-0956.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Starex TF-0956 is a Polymethyl Methacrylate Acrylic product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 220°C/10.0 kg | 6.0 | g/10 min | |
| 230°C/3.8 kg | 3.0 | g/10 min | |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.30 to 0.37 | % | |
| Across Flow : 3.20 mm | 0.35 to 0.42 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785, ISO 2039-2 | |
| Pencil Hardness 1 | H | JIS K5401 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2200 | MPa | ASTM D638 |
| -- | 2500 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 3 | 51.0 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/50 |
| Break 4 | 45.0 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 5 | 50 | % | ASTM D638 |
| Break | 17 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 6 | 2000 | MPa | ASTM D790 |
| -- 7 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 8 | 74.0 | MPa | ASTM D790 |
| -- 9 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10(23°C) | 4.7 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 49 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 44 | J/m | ASTM D256 |
| 23°C 11 | 3.9 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 90.0 | °C | |
| Desiccant Dryer | 90.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 500g |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 5.0 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.8 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | Thickness: 4 mm |
| 11 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-8732R | Teknor Apex Company | TPE | Telcar® |
| Sunny® PBT EB230-039 | Guangdong Shunde Shunyan New Material Co., Ltd. | PBT | Sunny® |
| ABSCOM® S160 | Polymer Compounders Limited | ABS | ABSCOM® |
| Evermore PUR SA-2066HR | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| E-RIALGLASS H 15 S 30 G | RIALTI Srl | PP Homopolymer | E-RIALGLASS |