High Temperature material (RGD525) has exceptional dimensional stability for thermal function testing of 3D models. The material has a heat deflection temperature (HDT) of 63-67 °C (145-153 °F) upon removal from the printer which can be increased to 75-80 °C (167-176 °F) after thermal post-treatment in a programmable oven. Ideal for:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 to 1.18 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 1.2 to 1.4 | % | ASTM D570 |
| Ash Content | 0.38 to 0.42 | % | USP 281 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 78 to 83 | ||
| Durometer Hardness (Shore D) | 87 to 88 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 to 3500 | MPa | ASTM D638 |
| Tensile Strength | 70.0 to 80.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 to 15 | % | ASTM D638 |
| Flexural Modulus | 3100 to 3500 | MPa | ASTM D790 |
| Flexural Strength | 110 to 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 14 to 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed 1 | 75.0 to 80.0 | °C | |
| 0.45 MPa, Unannealed | 63.0 to 67.0 | °C | |
| 1.8 MPa, Unannealed | 55.0 to 57.0 | °C | |
| Glass Transition Temperature | 62.0 to 65.0 | °C | DMA |
| Note Message | |
|---|---|
| 1 . | After thermal post treatment procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOPAS® 5013S-04 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| Trademark PE LLD2025G | Trademark Plastics Corporation | LLDPE | Trademark PE |
| ALTECH® PP-H A 2040/159 GF40 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| APEX® 97-G0029C-82 | Teknor Apex Company | PVC, Flexible | APEX® |
| IROSTIC® M 8304 | Huntsman Corporation | TPU, Unspecified | IROSTIC® |