STERLENE™ CMV207E
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | R&P (Pte.) Ltd. |
| Trademark: | STERLENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uk34wy_STERLENE-CMV207E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STERLENE™ CMV207E is a compound with high stiffness and medium impact designed for interior trim application. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 19 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2740 | MPa | ISO 527-2/50 |
| Tensile Stress (Yield, 23°C) | 27.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 5.1 | % | |
| Break, 23°C | 15 | % | |
| Flexural Modulus 2(23°C) | 2380 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Complete Break) | 7.1 | kJ/m² | ISO 179/A |
| Notched Izod Impact Strength (23°C, Complete Break) | 7.6 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 58.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 240 | °C | |
| Mold Temperature | 25.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure B |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene GC43P250-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Tarnamid® T- 27 MT 40 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| VALOX™ 815F resin | SABIC Innovative Plastics Asia Pacific | PBT+PET | VALOX™ |
| LNP™ THERMOCOMP™ RF009S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| LEXAN™ 201R resin | SABIC Innovative Plastics | PC | LEXAN™ |