TIPELIN® BS 520-14
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPELIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uh1EBV_TIPELIN-BS-520-14.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HDPE for blow moulding TIPELIN BS 520-14 is a high density polyethylene copolymer (with hexen-1 as comonomer) grade for blow moulding of products, which require very high ESCR and chemical resistance. The grade contains antioxidants and acid scavenger. Applications TIPELIN BS 520-14 is recommended for hollowed products of maximum 220 litres capacity for aggressive industrial chemicals and surface active substances, thermoforming of extruded sheets. TIPELIN BS 520-14 is suitable for food contact. The product complies with Food Contact Regulations. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.952 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.10 | g/10 min | |
| 190°C/21.6 kg | 10 | g/10 min | |
| 190°C/5.0 kg | 0.45 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, F50) | 630 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1500 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| Yield | 27.0 | MPa | |
| Break | 37.0 | MPa | |
| Tensile Elongation (Break) | 1400 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 28 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 128 | °C | ISO 306/A120 |
| Oxidation Induction Time (200°C) | 90 | min | EN 728 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blow Molding Temperature | 190 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRILOY AC3250 | Formosa Plastics Corporation | PC+ABS | TAIRILOY |
| NEXT REPROCESSED POMC M270-100R | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REPROCESSED |
| Braskem PE HF2207B5 | Braskem | LLDPE | Braskem PE |
| Chemlon® 125-15 MGHU | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Durethan® BG 30 X W1 000000 | LANXESS GmbH | Nylon 6 | Durethan® |