Starpylen HZ 30WF2
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starpylen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ugvEDQ_Starpylen-HZ-30WF2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starpylen HZ 30WF2 is a 30% Wood Fiber Reinforced Polypropylene Injection Molding Resin (also known as HZ30WF2). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 29.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2 |
| Flexural Modulus | 2680 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 1(23°C) | 17 | kJ/m² | ISO 179/1eU |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 185 to 195 | °C | |
| Middle Temperature | 185 to 195 | °C | |
| Front Temperature | 185 to 195 | °C | |
| Processing (Melt) Temp | 185 to 195 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 80*10*4 sp=62mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riteflex® 425 | Celanese Corporation | TPC-ET | Riteflex® |
| Udel® P-1700 LCD | Solvay Specialty Polymers | PSU | Udel® |
| Zytel® 77G33L BK031 | DuPont Performance Polymers | Nylon 612 | Zytel® |
| Mylar® WC (92 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Sylvin 4225-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |