KOPA® KN133G30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ugICKI_KOPAKN133G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Middle viscosity, G/F 30% reinforced Polyamide6 Compound resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow | 0.64 | % | ISO 294-4 |
| Flow | 0.34 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 3.0 | % | ISO 62 |
| Balance | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 120 | ASTM D785 | |
| R scale | 118 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| 23°C | 172 | MPa | ASTM D638 |
| 23°C | 170 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 9.0 | % | ASTM D638 |
| Fracture, 23°C | 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 8430 | MPa | ASTM D790 |
| 23°C | 7400 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 274 | MPa | ASTM D790 |
| 23°C | 240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 205 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 192 | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Arc Resistance | 130 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80 - 100 | °C | |
| Drying Time - Desiccant Dryer | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 230 | °C | |
| Middle Temperature | 245 | °C | |
| Front Temperature | 250 | °C | |
| Nozzle Temperature | 255 | °C | |
| Mold Temperature | 60 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP620Q | Southern Polymer, Inc. | LLDPE | PRIMALENE |
| Alathon® M6080UV | LyondellBasell Industries | HDPE | Alathon® |
| Elastron® V V101.D35.N | Elastron USA, Inc. | TPV | Elastron® V |
| INTEGRAL™ 630 | The Dow Chemical Company | Polyolefin, Unspecified | INTEGRAL™ |
| LNP™ LUBRICOMP™ DFL36 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |