Order Products : sales@su-jiao.com
Polylink Polymer P-11030-CT
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Polylink Polymers (India) Ltd. |
| Trademark: | Polylink Polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ufkOwt_Polylink-Polymer-P-11030-CT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Filled Polypropylene compounds are manufactured by compounding Polypropylene with fine fillers (i.e. mica, chalk, talc, glass). Additives like antioxidants, lubricant, processing aid and desiccant are added to improve long term thermal and processability. The compounds used directly or diluted with desired grades of polypropylenes show good dispensability and excellent balance of properties in the ultimate product. The fillers in the compound incorporates certain important properties those are essential for ultimate product. The modification are as below. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | Internal method |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 - 9.0 | g/10 min | ASTM D1238 |
| Moisture Content | < 600 | ppm | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 18.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 2350 | MPa | ASTM D790 |
| Flexural Strength | 28.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 49 | J/m | ASTM D256 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 0.50 | hr | |
| Cylinder Zone 1 Temp. | 190 | °C | |
| Cylinder Zone 2 Temp. | 200 | °C | |
| Cylinder Zone 3 Temp. | 210 | °C | |
| Cylinder Zone 4 Temp. | 215 | °C | |
| Cylinder Zone 5 Temp. | 220 | °C |
| Extrusion instructions |
|---|
| Zone 6 : 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Q281 (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| Unichem 4160C | Colorite Polymers | PVC, Unspecified | Unichem |
| Comai 725-2 NT | Comai Ltda | LLDPE | Comai |
| Fluoroloy® A15 | Saint Gobain Performance Plastics | TP, Unspecified | Fluoroloy® |
| Generic Nylon 66+Nylon 6I/X | Generic | Nylon 66+Nylon 6I/X | Generic |