SCHULAMID® 6 NV SI
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ufcDgI_SCHULAMID-6-NV-SI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low viscosity Polyamide 6 Compound |
| General Information | |
|---|---|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2850 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 73.0 | MPa | |
| Break | 65.0 | MPa | |
| Tensile Strain (Yield) | 4.2 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 9.0 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 2650 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| 3.5% Strain | 85.0 | MPa | |
| 6.4% Strain | 104 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.4 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 215 | °C | ISO 306/A50 |
| -- | 190 | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1600.5 L MG 15 | RTP Company | PAS | RTP |
| RONFALIN® FF50AM | A. Schulman Europe | ABS | RONFALIN® |
| Stanyl® 46HF4530 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| UBE Nylon 5033 B | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| CarmelStat™ CS 2015 | Carmel Olefins Ltd. | PP, Unspecified | CarmelStat™ |