LNP™ THERMOCOMP™ D151 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uegAyC_LNP-THERMOCOMP-D151-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Thermocomp* D151 (experimental grade name as EXTC8274) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good surface, good flatness, good ductility, Non-Brominated & Non-Chlorinated Flame Retardant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 300°C/1.2 kg | 14 | g/10 min | |
| 300°C/2.16 kg | 29 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 300°C/1.2 kg | 13.0 | cm³/10min | |
| 300°C/2.16 kg | 27.0 | cm³/10min | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 0.30 to 0.50 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.080 | % | |
| Equilibrium, 23°C, 50% RH | 0.040 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4400 | MPa | ASTM D638 |
| -- | 4430 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 83.0 | MPa | ASTM D638 |
| Break | 82.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 3.6 | % | ASTM D638 |
| Break | 3.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 4070 | MPa | ASTM D790 |
| -- 5 | 4010 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 133 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 8(23°C) | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 710 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 22.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 121 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 117 | °C | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 3.4E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 7.7E-5 | cm/cm/°C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant | Internal Method | ||
| 1.10 GHz | 3.07 | ||
| 1.90 GHz | 3.06 | ||
| 5.00 GHz | 3.06 | ||
| 10.0 GHz | 3.05 | ||
| Dissipation Factor | Internal Method | ||
| 1.10 GHz | 6.7E-3 | ||
| 1.90 GHz | 6.5E-3 | ||
| 5.00 GHz | 6.9E-3 | ||
| 10.0 GHz | 6.9E-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.300 mm | V-2 | ||
| 0.400 mm | V-1 | ||
| 0.600 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 285 to 305 | °C | |
| Processing (Melt) Temp | 285 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Back Pressure | 0.100 to 0.300 | MPa | |
| Screw Speed | 50 to 90 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 sp=62mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 300 GF4 TF3 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| NEXUS Reprocessed ABS Black Repro | Nexus Resin Group, LLC. | ABS | NEXUS Reprocessed |
| Delrin® 511DP BK402 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| INEOS LLDPE LL6808AA | INEOS Olefins & Polymers Europe | LLDPE | INEOS LLDPE |
| LEXAN™ 241R resin | SABIC Innovative Plastics | PC | LEXAN™ |