Clear-Flex® FF 506
| Category: | LMDPE , Linear Medium Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clear-Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | udogNV_ClearFlexFF506.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex FF 506 is an hexene copolymer linear medium density polyethylene (C6-LMDPE), with antioxidants and processing aid, suitable for blown film extrusion. Film manufactured with Clearflex FF 506 are characterized by high rigidity and temperature resistance, good sealing properties. Main Applications Clearflex FF 506 is characterized by good mechanical and sealing performances, it is recommended for applications in which the high rigidity of this resin is a key factor (hygienic film and packaging for mineral water). The high Vicat softening point makes Clearflex FF 506 ideal for the production of film for food which is submitted to pasteurisation or sterilisation process. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.934 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 10 to 50 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% secant, MD : 25 µm, blown film | 400 | MPa | ISO 527-3 |
| 1% secant, TD : 25 µm, blown film | 450 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, blown film | 16.0 | MPa | ISO 527-3 |
| TD : Yield, 25 µm, blown film | 18.0 | MPa | ISO 527-3 |
| MD : Broken, 25 µm, blown film | 50.0 | MPa | ISO 527-3 |
| TD : Broken, 25 µm, blown film | 40.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 25 µm, blown film | 550 | % | ISO 527-3 |
| TD : Broken, 25 µm, blown film | 700 | % | ISO 527-3 |
| Dart Drop Impact (25 µm, Blown Film) | 80 | g | ISO 7765-1/A |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 25.0 µm | 40.0 | kN/m | ISO 6383-2 |
| TD : 25.0 µm | 200.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 118 | °C | ISO 306/A |
| Melting Temperature | 128 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 14 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL6R 805 | Marco Polo International, Inc. | LLDPE | MARPOL® |
| RTP EMI 332D FR | RTP Company | PC | RTP |
| Spartech Polycom EP6410 B149 | Spartech Polycom | PP, Unspecified | Spartech |
| Karina GRAY PVC COMPOUND 700D18/234-C-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ADLEN® J01BG-04 | A.D. Compound S.p.A. | PP Copolymer | ADLEN® |